17-4 Stainless Steel Bar UNS S17400 (Grade 630)

17-4 stainless steel bar is one of the original precipitation hardened grades developed in the 50’s. Primarily comprised of 17% chromium, 4% nickel, 4% copper, with the balance being iron. Other characteristics include high strength, toughness, and quality mechanical properties at temperatures up to 600° F. Engineers and designers frequently choose Stainless Steel 17-4 PH due to its high strength and superior corrosion resistance when compared to many other stainless steels.

Aamor-Inox 17-4 material offers following benefits:

High Tensile Strength and Toughness
High Hardness upto 600? F (316?C)
Excellent Corrosion Resistance.

Aamor-Inox’s produces 17-4 materials to meet the following specification: AMS 5643R, DIN/EN 10088-3, AMS 5622, ASTM A564

CHEMCIAL COMPOSITION (AVERAGE %)

Grade	C (Max)	Si (Max)	Mn (Max)	Cr	Ni	CU	Bn + Ta	S (Max)	Ph (Max)	MO (Max)rade
17-4	0.07	1.00	1.00	15.00-17.50	3.00-5.00	3.00-5.00	0.15 to 0.45	0.030 (0.025)	0.040 (0.030)	-
630	0.07	1.00	1.00	15.00-17.50	3.00-5.00	3.00-5.00	0.15 to 0.45	0.030 (0.025)	0.040 (0.030)	-
1.4542	0.07	0.70	1.50	15.00-17.50	3.00-5.00	3.00-5.00	5xC to 0.45	0.030 (0.025)	0.040 (0.030)	0.60
1.4548	0.07	1.00	1.00	15.00-17.50	3.00-5.00	3.00-5.00	0.15 to 0.45	0.025	0.025	0.60

* Ph upto 0.025% max can be achieved and supplied as per ASME 5622. PREN = (%Cr+3.3%Mo+16%N) > 17

MECHANICAL PROPERTIES

Type	Standard	Tnsile Strenth(min)		Yield Stranth(min)		Elongation% (min)	Reduction (min)	Hardness				Empact Charpy-V (min)
		Tnsile Strenth(min)		Yield Stranth(min)				Rockwell C		Brinell		Foot/Lbs	Joules
		KSI	MPA	KSI	MPA			Min	Max	Min	Max
Condition A	ASTM A564	-	-	-	-	-	-	-	38	363	363	-	-
H900	ASTM A564	190	1310	170	1170	10	40	40	-	388	-	-	-
H925	ASTM A564	170	1170	155	1070	10	44	38	-	375	-	5	6.8
H1025	ASTM A564	155	1070	145	1000	12	45	35	-	331	-	15	20
H1075	ASTM A564	145	1000	125	860	13	45	32	-	311	-	20	27
H1100	ASTM A564	140	965	115	795	14	15	31	-	302	-	25	34
H1150	ASTM A564	135	930	105	725	16	50	28	-	277	-	30	41
H1150M	ASTM A564	115	795	75	520	18	55	24	-	255	-	55	75
H1150D	ASTM A564	125	860	105	725	16	50	24	-	255	311	30	41
Condition AT	EN 10088-3	-	1200 max	-	-	-	-	-	-	-	360	-	-
P800	EN 10088-3	-	800-950	-	520	18	-	-	-	-	-	-	75
P930	EN 10088-3	-	930-1100	-	720	16	-	-	-	-	-	-	40
P960	EN 10088-3	-	960-1160	-	790	12	-	-	-	-	-	-	-
P1070	EN 10088-3	-	1070-1270	-	1000	10	-	-	-	-	-	-	-

Corrosion Resistance

Material withstands corrosion better than any other standard hardenable stainless steels
Stress corrosion cracking resistance is developed by age hardening at temperatures of 1025?F (552?C) and higher
Aamor-Inox’s 17-4 material has good resistance to sulfide stress cracking at Rockwell C 33 maximum hardness as per NACE MR-01-75

Products Available in Grade 17-4ph

Size Range	Size (diameter)		Size (diameter)	Size (diameter)
Size Range	mm	Inch	Size (diameter)	Size (diameter)
Bright Round Bars	15 – 150	5/8”- 5-3/4”	h9, h11, K12, K13	upto 24 feet / 7 meters
Pump Shaft Quality Bars	15 – 100	5/8” to 4”	h6, h7, h8, h9	upto 24 feet / 7 meters
Boat Shaft Quality Bars	15 – 100	5/8” to 4”	h6, h7, h8, h9	upto 24 feet / 7 meters
HRAP Flat Bars	25x3 – 150x50mm	5/8”, 7/8”, 1”, 1.1/4”, 1.1/2, 2””	ASTM A484 (Table4) /EN 10059	upto 24 feet / 7 meters

Round Bars

Precision & Accuracy Round Bars

Cold Drawn Profiless

HRAP Profiles & Wire Rods